Resolve resolution of Manganese silicide:

2 g (0.036 mol) of manganese, 2 g (0.071 mol) of silicon and 10 g (0.16 mol) of copper were placed in a small block into a 10 mL Al2O3 crucible and placed in an open ampoule ampoule.
After evacuation and fouling, place the ampoule in a carbon and silicon rod.
The temperature was raised to 1200 ° C in 12 h and then cooled to 500 ° C at a rate of 10 ° C / h. The ampoule is removed, cooled, and then inserted into a thicker rubber tube, breaking the ampoule so that the metal ingot can be safely removed.
The copper-rich Cu-Mn-Si block was dissolved in 8 mol / L nitric acid. The octahedral crystals were left and the crystals were washed with water and dried to obtain MnSi2 crystals with an edge length of 2 mm.
Several octahedral crystals were pulverized and studied using Guinier-Hagg (Cu-ray).
(Α = (4.560 ± 0.001) A · (1A · = 0.1 nm, the same below) this value is allowed to be tested in the past reported MnSi2 lattice (4.558 ± 0.001) . Within the error range.
Since the finely divided crystals and past products have very similar lattice constants, it indicates that most of the manganese is not replaced by copper. This result is also confirmed by the emission spectrum analysis of the crystal, indicating that the upper limit of copper content is about 1%.

Feature of Manganese silicide:

Physical properties: gray octahedral crystal, density (g / mL, 25 ℃): 5.24, soluble in hydrofluoric acid, alkali, insoluble in water, nitric acid, sulfuric acid. The following are the same as the "

Item Appearance Particle size
Density (g/mL,25℃)
Molecular weight
gray octahedral crystals

1-10um 99.5%, 60-325 mesh 99.5%


Storage and transportation of Manganese silicide:

Keep the receptacle sealed, placed in a tight container, stored in a cool, dry place

Packing: 1 kg / vacuum pack, 25 kg / drum